Microhardness testing providers with MicroVision Laboratories right now? The scan from left to right shows a high tin concentration (green line) while areas of higher lead concentrations (blue line) were not intersected by the line scan. At the interface between the tin/lead solder and copper (red line), there is a mixture of the solder and copper which is the intermetallic layer. The EDS Map provides a nice visual mixture of colors which shows the intermetallic layer while the line scan clearly shows the intermetallic with the elemental graph.
Conclusion: Based on the analytical report, the client was able to demonstrate that the particles were consistent with a common aspirin tablet. When the end customer was approached with this report, they remembered that their spouse had taken an aspirin earlier that morning, and had likely used the bottle of water in question to do so. Based on this, the customer was happy, the manufacturing client was satisfied, and the sample was maintained – undestroyed should someone need to examine the sample again or do any more esoteric testing. For an affordable price, the client was able to get piece of mind, and gather information from a very wide range of testing methods quickly and accurately.
Dust samples were analyzed using polarized light microscopy (PLM) to provide percentages of the particle types present in the samples. MVL was able to determine that there was significant loading of glass fibers in the dust samples with the likely source being contractor’s work in the attic which involved disturbing the fiberglass insulation. The image on the right shows a few distinct glass fibers with a binder material adhered to them, consistent with fiberglass insulation.
MicroVision Laboratories, Inc. has been providing businesses, consultants and other testing laboratories with expert microscopy and analytical services since 2003. Our client base covers a broad spectrum of industries including semi-conductors, aerospace, electronics, biomedical, ceramics, optics, pharmaceuticals, mineralogy, metallurgy, thin films, environmental, membranes filtration and industrial hygiene. Discover a few extra info on Microvisionlabs.com.
What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times.
SEM is a powerful surface microscopy method which allows for high resolution images to be obtained on a wide range of samples. A focused beam of electrons sweeps across a sample surface and an image is created from the scattered electrons. The electron beam allows for the accurate imaging of features below the resolution limit of visible light. The acquired pictures retain good depth of field, resulting in excellent three-dimensional images. Variations in beam parameters can be made in order to highlight variations in density in the target sample, show extremely fine surface features, and illustrate texture in sample surface coatings. MicroVision Labs has multiple fully-operational SEMs, Bruker X-Flash EDS detectors and mapping technology, backscatter electron (BSE) imaging, and large chamber capabilities. These provide a full suite of microscopy services for all of your analytical needs. See even more info at https://microvisionlabs.com/.