A few welding supplies handbook: how to become a better welder and how to pick the top welding equipment. Use the smallest tungsten that will get the job done. Use the smallest tungsten to get the job done. …within reason. Another way of saying this is don’t just use a 1/8” electrode for everything. There are jobs where a 1/8” electrode is great like for welding 3/16” thick aluminum. But what if you are welding on the edge of a .030” turbine blade? A .040” electrode will be plenty to handle the 15 amps and will give much better starts than even a 1/16” electrode. Too large an electrode can cause an erratic arc and contamination…and A bad start where the high frequency tries to arc up inside the cup and off the side of the tungsten can easily melt off a thin edge and scrap an expensive part. 2% thoriated or lanthanated tungsten electrodes hold up at high amperage better than most all other electrodes. When welding at higher amperages, often times you can use one size smaller electrode by using 2% thoriated or lanthanated. And that is a good thing.
Don’t use too much torch gas when welding aluminum on A/C. Don’t use too much torch gas when welding aluminum on A/C. Aluminum takes a lot of amperage to weld. Even though the melting temperature of aluminum is less than half that for steel, it takes about twice as much amperage to weld. Why? Because aluminum conducts heat away from the weld puddle faster than you can put it in. this brings me to an important point. Do not use more argon than necessary on your torch gas. If you do, it will be like blowing cool air on something you are trying to heat up with a torch. All that argon blowing on the part makes for a loud erratic arc because the arc force is so great. Have you ever lit up on a thick aluminum casting and listened to how loud the arc is? I bet your torch gas was up around 20 like the books recommend. That’s too much for aluminum (unless you are using an argon helium mix).
Make sure everything is ‘squeaky’ clean. TIG welding is not tolerant of any contaminants. Be sure to clean your base metal with a good degreaser, BEFORE you scrub it with a dedicated wire brush. Do not use the same brush on different kinds of metal. Wipe the filler rod down with degreaser, too. Get comfortable. Whenever possible, I like to be seated when I’m welding. Even in situations where sitting isn’t possible, any little adjustments to my stance or body position that make me more comfortable will have a noticeable effect on the weld.
Looking for the best Welding Equipment? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Following some simple tips can help you take your MIG welding operation to the next level and ensure you are as safe, efficient and professional as any other shop. Welding helmets, gloves, close-toed shoes and clothes that fully cover exposed skin are essential. Make sure you wear flame-resistant natural fibers such as denim and leather, and avoid synthetic materials that will melt when struck by spatter, potentially causing burns. Also, avoid wearing pants with cuffs or shirts with pockets, as these can catch sparks and lead to injuries.